    电容器可靠性测试


    t1.jpg



    项目


    性能要求

    试验方法

    耐电压(TV)

    两引线间

    无击穿或飞弧

    两引线间施加50/60H  Y1:4000VAC/ 60秒 Y2:2500VAC/60秒;最大泄露电流50 mA

    引线与外表

     将电容器的两条引线连接在一起,本体部分插入装有小金属球容器内(金属球与引线间的距离不小于1.5mm),在金属球与引线之间施加50/60Hz (Y1:4000VAC/60秒;Y2:2500VAC/60秒)

    绝缘阻抗(I.R.))

    ≥10000MΩ

    将电容器两引线间施加500VD,充电时间60±5秒

    静电容量和误差
         (CAP&Tolerance)

    规定的容量和误差范围内

    测试频率:1±0.2KHz   测试电压: 1.0±0.2    Vrms (20±2℃)

    损耗角正切(tgδ)

    ≤250×10-4

    测试条件与静电容量相同


    Item

    Performance

    Test  Method

    Withstand    Voltage(TV)

     

    Between    Terminals

    Should be    no remarkable and abnormality

    Apply    Y1:4000VAC;Y2:2500VAC/60sec ;charge/discharge current should not exceed 50A

    Between    Terminials and Encloser

    Insert the    capacitor body filled with a diameter of 1 mm metal ball in the container,but    keep away from the end of 2mm ontology is not inserted;Test voltage applied    between the short circuit loop terminal and a metal ball

    Insulation
                    Resistance(I.R.)

    ≥10000MΩ

    Applied    5OOVDC between two terminals ,duration:5 second

    Capacitance
    (C)&    Tolerance

    W it hi n the    specified tolerance

    Measuring    Frequency:1±0.2KHz
    Measuring    voltage: 1.0±0.2    Vrms (20±2℃)

    Dissipation Factor    (DF)

    ≤250×10-4

    Method    same with Capacitance



    t2.jpg


    项    目

    性能要求

    试验方法

    引线引出端强度

    拉力

    符合电性能规定,引线无断裂或松落
                   

    将电容器其中一根引线于径向方向施加下列荷重(参照IEC-68-2-20):荷重1K g;时间10±1.0秒

    弯曲

    将电容器其中一根引线于径向方向施加0.5K g荷重施加两个循环; 每个循环引线于两端子间弯曲90º,复位2~3秒;然后向相反方向弯曲90º复位

    Item

    Performance

    Test     Method

    Terminal  strength

    Tensile

    Should satisy electrical    characteristics;the terminals should be not break or loose

    Apply one lead the    specified strength(Refer to IEC-68-2-20):Load 1Kg; Duration:10±1.0Sec

    Bending

    Apply    one lead the 0.5Kg for two cycles;Each cycle     includes:90º once,Return to its initial position for 2~3 Sec,and then to the opposite direction    once

     

    t3.jpg


    项目

    性能要求

    试验方法

    可焊性

    外观

    均匀覆盖引线浸入部分95%以上

    焊锡温度:235±5℃  浸入时间: 2.5±0.5S
         浸入速度: 25±6mm/s

    耐焊接热

    外观

    无可见的损伤或异常

    预热温度:100~120℃
         预热时间:60秒内
         温度上升率不超过2 ℃/秒
         焊锡温度260±5℃, 浸入时间10±0.5Sec.
         浸锡深度:引线根部起4±0.8mm
         试验后处理:电容器置于标准大气压条件下放置24±2小时后再进行测量

    容量变化率

    ±10%    (Y5P)
         ±15%(Y5U )
         ±20%(Y5V )

    耐电压
         (引线之间)

    符合耐电压规定

    损耗角正切

    ≤250×10-4   (1±0.2KHz,1.0±0.2 Vrms,20±2℃)

    绝缘阻抗

    ≥5000 MΩ(500V60秒,20±2℃)

     湿热试验

    外观

    无可见的损伤或异常

    温度:40±2℃
         湿度:90~95%
         存放时间:500+24小时。
         试验后处理:电容器置于标准大气压条件下放置1~2小时后再进行测量

    容量变化率

    ±10%    (Y5P)
         ±15%(Y5U )
         ±20%(Y5V )

    耐电压
         (引线之间)

    符合耐电压规定

    损耗角正切

    ≤5.0×10-4  (Y5P、Y5U)
         ≤7.5×10-4    (Y5V)
         (1±0.2KHz,1.0±0.2 Vrms,20±2℃)

    绝缘阻抗

    ≥5000 MΩ(500V60秒,20±2℃)

    Item

    Performance

    Test     Method

    Solderability

    Apperance

    Should be no remarkable change

    Soldering Temperature: 235±5℃
    Immersion Duration: 2.5±0.5S
    Immersion Duration: 25±6mm/s

    Soldering    Heat Resistance

    Apperance

    Should    be no remarkable change

    Preheat Temperature:100~120℃
    Preheat Duration:60 Sec. max
    Temperature Increase by 2℃/sec. max
    Soldering Temperature:+260±5℃
    Immersion    Duration: 10±0.5Sec
    Immersion depth: 4±0.8mm from the roots
    After    test,allow it stay alone for 24±2 Hours
    at standard temperature and humidity before    making measurement

    Capacitance    Change Rate(△C/C)

    ±10% (Y5P)
    ±15%(Y5U )
    ±20%(Y5V )

    Withstand    Voltage
    (Between    Terminals)

    Shall    satisfy withstand voltage

    DissipationFactor

    ≤250×10-4 (1±0.2KHz,1.0±0.2 Vrms,20±2℃)

    Insulation    Resistance

    ≥5000 MΩ(500V 60Sec,20±2℃)

    Humidity    Heat Resistance

    Apperance

    Should    be no remarkable change

    Temperature: 40±2℃
    Humidity: 90~95%RH
    Storage Duration:500+24Hours
    After    test,allow it stay alone for 1~2 Hrs
    at standard temperature and humidity before    making measurement

    Capacitance    Change Rate(△C/C)

    ±10% (Y5P)
    ±15%(Y5U )
    ±20%(Y5V )

    Withstand    Voltage
         (Between    Terminals)

    Shall    satisfy withstand voltage

    DissipationFactor

    ≤5.0×10-4  (Y5P、Y5U)
    ≤7.5×10-4    (Y5V)
    (1±0.2KHz,1.0±0.2    Vrms,20±2℃)

    Insulation    Resistance

    ≥5000 MΩ(500V 60Sec,20±2℃)

    项目

    性能要求

    试验方法

    耐久性试验

    先施加三次脉冲如下:

    three.jpg                

    外观

    无可见的损伤或异常

    温度:85±3℃40±2℃下施加负载:50Hz/60Hz 425 Vrms (Y2) or 680Vrms(Y1)
    持续时间:1000小时
    并每小时将电压升高到1000VAC,持续时间0.1s。。
    试验后处理:
    电容器置于标准大气压条件下放置24±2小时后再进行测量

    容量变化率

    ±20%

    耐电压
    (引线之间)

    符合耐电压规定

    损耗角正切

    ≤5.0×10-4  (Y5P、Y5U)
    ≤7.5×10-4    (Y5V)
    (1±0.2KHz,1.0±0.2 Vrms,20±2℃)

    绝缘阻抗

    ≥5000 MΩ(500V60秒,20±2℃)

    Item

    Performance

    Test     Method

    Long Life Testing

    Pre-Loading    3 times to the capacitor by puls voltage

    three.jpg                

    Apperance

    Should    be no remarkable change

    Temperature:85±3℃40±2℃
    Voltage Loading: 425 Vrms (Y2) or 680Vrms(Y1) 50Hz/60Hz
    Duration:1000    Hrs AC Voltage up to1000V ,
    Consistance    time:0.1sec
    After test,allow it stay alone for    24±2Hrs at standard temperature and humidity before making measurement

    Capacitance    Change Rate(△C/C)

    ±20%

    Withstand    Voltage
     (Between    Terminals)

    Shall    satisfy withstand voltage

    DissipationFactor

    ≤5.0×10-4  (Y5P、Y5U)
    ≤7.5×10-4    (Y5V)
     (1±0.2KHz,1.0±0.2 Vrms,20±2℃)

    Insulation Resistance

    ≥5000 MΩ(500V60sec,20±2℃)